ductile fracture surface【力】 韧性断口文献(pubmed) 赞助商链接以下为句子列表:英文: Bonding mechanism of crosshead ductile iron surface and tin pewter layer中文: 十字头球铁表面与锡锑轴承合金层结合机理 英文: From macroscopical to microcosmic, from qualitative to quantitative, from fracture surface ...
M. Ohashi, Extreme value analysis of ductile fracture surface by dimpled rupture associated with fracture behavior of tensile specimens, J. of Mat. Sci. 42 (2007) 9877-9887.Ohashi, M. 2007. Extreme value analysis of ductile fracture surface by dimpled rupture associated with fracture behavior ...
A ductile fracture is a type of fracture characterized by extensiveplastic deformationornecking. This usually occurs prior to the actual fracture. In a ductile fracture, there is absorption of massive amounts of energy and a slower propagation before the fracture occurs as compared to abrittle frac...
Copper NWs with a diameter of ∼600 nm exhibited approximately 30% plastic strain before fracture, whereas those with a diameter of ∼200 nm showed brittle-like fracture without remarkable plastic deformation and a rough fracture surface [117]. On the other hand, the ductile–brittle fracture...
分享到: 韧性断面率 分类: 科技词汇|查看相关文献(pubmed)|免费全文文献 详细解释: 以下为句子列表: 分享到:
It is well recognized in the literature that the fracture process of thin metal sheets involves three energy dissipation mechanisms i.e., plasticity, necking and surface separation. However, the complex stress state in thin structures hinders the experimental assessment of these quantities and, consequ...
Fully brittle fracture involves the rupture of interatomic bonds ahead of the crack, as illustrated in Fig. 18.7. This produces a fracture surface that can be close to atomically flat, called the cleavage fracture. A cleavage crack grows between the atomic planes along a specific crystallographic ...
(1) Under the condition of dynamic tensile, there is a brittle fracture feature in the local weak-link though the metals still show the ductile fracture feature.(2) The bright belt in the impact fracture surface is caused by the fatigue precrack blunt, a distribution of crack stretched zone...
the fracture surface sometimes appears smooth and polished. In a brittle overload failure, the crack will begin at a point of maximum stress, and then grow across the section. Separation of the two halves isn’t quite instantaneous, but crack speeds are very high, approaching the speed of so...
Scanning electron microscopy showing coarse dimples dominated ductile fracture surface in the quenched and partitioning heat treated microalloyed low carbon steel (a)–(c) caused by the presence of fine metalloids (d), respectively. Full size image The monotonic decline in the work hardening rate wit...