Large sized, lightweight building element with a density of 1000-1400 kg/m3 is produced by hydrothermally curing a mixt of 14-18% wt calcined lime with a particle size 0.1 mm 6-12% wt ground fine sand with a particle size 0.2mm. 38-44% wt. underground sand with a particle size 1.0...
Large sized, lightweight building element with a density of 1000-1400 kg/m3 is produced by hydrothermally curing a mixt of 14-18% wt calcined lime with a particle size 0.1 mm 6-12% wt ground fine sand with a particle size 0.2mm. 38-44% wt. underground sand with a particle size 1.0...
The heated fibers are compressed in a mold to an average density of about 800 kg/m3 to about 1600 kg/m3. Compression pressures of between 3,4 Mpa and 27,5 Mpa are used to achieve product densities within this range. The compressed fibers are cured under these temperature and pressure ...
The heated fibers are compressed in a mold to an average density of about 800 kg/m3 to about 1600 kg/m3. Compression pressures of between 3,4 Mpa and 27,5 Mpa are used to achieve product densities within this range. The compressed fibers are cured under these temperature and pressure ...
temperature at an elevated pressure, and is extruded through a die at rates in excess of 1000 kg/hr to produce an expanded and dimensionally-stable, predominantely closed cell propylene polymer foam with a density of between 10 kg/m3 and 150 kg/m3, and with a thickness in excess of 1.3 ...
Large sized, lightweight building element with a density of 1000-1400 kg/m3 is produced by hydrothermally curing a mixt of 14-18% wt calcined lime with a particle size 0.1 mm 6-12% wt ground fine sand with a particle size 0.2mm. 38-44% wt. underground sand with a particle size 1.0...
grossformatiger, dampfgehaerteter lightweight formkoerper the rohdichteklasse 1000 to 1400 kg \\/ m3 and methods for its manufactureKUNZE HEINZMENCKE HEINRICHBERENS LEO DR-ING
700 - 1000, kg/m3 and a particle size of 1 - 10 (esp. 1 - 4) mm. The product is suitable for treatment with HCl gas in fluidised beds to removed hydrolysis products such as MgO and MgOHCl and to dry the product still further, e.g. to 0.2 wt.% water content. The anhydrous ...