The deuterides Zr3V3B0.24O0.36D8.0 and Zr3V3B0.40O0.60D6.4 with cubic structures [space group Fd3m (No. 227)] related to 畏1- (Fe3W3C) type have been studied by powder X-ray and neutron diffraction. The transition from the alloys to the corresponding deuterides gives a redistribution ...
Upon cooling the molten mixture, the resulting black powder of the product sodium platinate was purified and conductivity and powder diffraction studies were carried out [1]. Conductivity measurements showed that the product phase NaPt3O4 was a good sodium ion conductor (specific resistance at room...