A Cu-Cr-Zr-Mg alloy was prepared with spray forming technology. The microstructure was observed and the microhardness, tensile strength and electrical conductivity of alloy after thermal mechanical processing were tested at ambient temperature. The results show that the good combination of high ...
步骤1,制备cu-zr中间合金; 步骤2,制备cu-cr-zr-mg合金: 将cu块、cu-zr中间合金、cr粒和mg粒由下至上依次放置在坩埚中,在真空感应炉内,氩气保护下,进行熔炼,冷却,得到cu-cr-zr-mg合金; 步骤3,cu-cr-zr-mg合金热处理: 对步骤2得到的cu-cr-zr-mg合金进行固溶、时效热处理,即得到cu-cr-zr-mg合金成品...
快速凝固Cu 合金由于具有高的过饱和度,大量的空位以及细小的晶粒;在其形变后的时效过程中,析出行为对再结晶过程的影响与常规Cu合金大不相同 。本文研究了快速凝固Cu2Cr2Zr2Mg合金 再结晶与时效析出的交互作用,并从热力学上 进行了分析。1 实验方法 将Cu20.6Cr20.15Zr20.5Mg合金20g放入 喷嘴直径为0.6mm的石英...
Cu-Cr-Zr-Mg-RE合金 1. Microstructure and properties of aging Cu-Cr-Zr-Mg-RE alloy; 时效态Cu-Cr-Zr-Mg-RE合金的组织与性能 2. Melting technique of Cu-Cr-Zr-Mg-RE alloy with high performance in air was discussed. 探讨了高性能Cu-Cr-Zr-Mg-RE合金在大气下的熔炼技术。3...
本发明公开了一种CuCrZrMg合金棒材的制备方法,具体为:Cu块,Cr粒,Mg条和CuZr中间合金按依次放入石墨坩埚中感应熔炼,得到CuCrZrMg合金液;将合金液浇注在细直径铜模具中快速冷却,得到CuCrZrMg合金棒材;对棒材进行固溶,时效热处理,经机械加工,即得到CuCrZrMg合金棒材成品.本发明通过在传统CuCr合金中引入Zr元素与Mg元素,...
探讨了引线框架Cu-Cr-Zr-Mg合金固溶后二级变形时效工艺对合金硬度和电导率等性能的影响规律。2) Cu-Cr-Zr-Mg-RE alloy Cu-Cr-Zr-Mg-RE合金 1. Microstructure and properties of aging Cu-Cr-Zr-Mg-RE alloy; 时效态Cu-Cr-Zr-Mg-RE合金的组织与性能 2. Melting technique of Cu-Cr-Zr-Mg-RE all...
通过透射电镜和高分辨透射电镜研究 Cu-0.69Cr-0.10Zr-0.02Mg 合金在450℃早期时效的析出贯序。研究表明:合金在450℃早期时效的析出贯序为过饱和固溶体→溶质偏聚→FCC富Cr的GP区(Ⅰ)→FCC有序富Cr的GP区(Ⅱ)→BCC有序富Cr相。在脱溶演变过程中,析出相和基体之间的界面由完全共格界面向... 查看全部>> ...
摘要: 研究了固溶时效和快速凝固时效工艺对Cu-Cr-Zr-Mg合金的显微组织,硬度和导电率性能的影响.结果表明快速凝固态晶粒比固溶态晶粒细小得多,细晶强化作用显著.合金经920℃×1h固溶和550℃×0.5h时效后,硬度为100HV,导电率这71%IACS;快速凝固和同样的时效条件下,硬度为126HV,导电率达70%IACS.关键词:...
一,前言黑色金属压铸是一项少无切削新工艺,它具有生产效率高,压铸件尺寸精度和表面质量好,晶粒组织细,表面纤维结构完整而整体机械强度高,材料利用率高且可减少机加工设备和工时等优点.所以几十年来,虽遇到很多困难,国外一直在试验研究,并在动态机械性能(如冲击,疲劳强度等)要求不高的十几种不锈钢另件上实现了批量生...