The anneal hardening behavior of a Cu-16 at. pct. Al alloy was investigated by tensile testing, measurement of Young's modulus and electrical resistivity, and electron microscopy. It was shown that three main stages of annealing processes can be distinguished. Stage 1 at T ≤ 150°C is ...
The anneal hardening behavior of a Cu-16 at. pct. Al alloy was investigated by tensile testing, measurement of Young’s modulus and electrical resistivity, and electron microscopy. It was shown that three main stages of annealing processes can be distinguished. Stage 1 atT ≤ 150°C is charac...
anneal hardeningCu-Al alloysolid solution alloybicrystal specimenVickers hardnessLow-temperature anneal hardening of a cold-worked Cu-Al solid solution alloy was investigated in single, bi- and polycrystals of Cu-13.5 at.-%Al alloy. In grains of a bicrystal specimen, where piled-up dislocations ...
Using correlated RHEED and STM data, we find a dramatic smoothing of epitaxial Cu(001) surfaces by anneal... RA Lukaszew,C Uher,R Clarke - 《Mrs Proceedings》 被引量: 0发表: 2000年 Unified Model for Structure Transition and Electrical Properties of InAs (001) Surfaces Studied by Scanning ...
2a). The process began under 750 mbar of nitrogen base pressure, had 1 °C/s heat up and cool down ramps, 10 min of RTP anneal at 520 °C and 1 min of sulfurization anneal under 50 mbar of pure H2S, at 550 °C. The resulting narrow BG is consistent with the ...
Interdiffusion in the Cu‐based Cu/Pd, Cu/Pt, Cu/Ni, Cu/NiB, Cu/Co, Cu/Cr, Cu/Ti, and Cu/TiN bilayer films has been investigated for anneal temperatures ranging from 150 to 400°C in forming gas (N2‐10%H2). The diffusion of Pd, Pt, and Ni into Cu has resulted in a signifi...
Therefore, we anneal the samples with slowly decreasing the temperature from 400 to 300 °C in our standard process. With this method, the sample is oxygenated to some extend at higher temperature where the diffusivity of oxygen is relatively fast, and then further oxygen is loaded into the ...
Melt-spun ribbons with composition Sm2+Y(Co0.8Fe0.1Mn0.1)17BX (X=0–1.0 and Y=0–0.2) were fabricated with a wheel speed of 50 m/s, followed by anneal... H D.,Kim,and,... - 《Journal of Magnetism & Magnetic Materials》 被引量: 7发表: 1998年 加载更多来源...
a全身都是泥 The whole body all is the putty[translate] a请输I opened my eyes last night and saw you in the low light Please lose I opened my eyes last night and saw you in the low light[translate] aelectrolytic TOUGH PITCH ANNEAL RESISTANT cu C11000B ETP电解坚韧沥青[translate]...
Anneal-induced enthalpy relaxation behaviour was examined calorimetrically for Zr 50-70 Cu 50-30 , Zr 70 (Cu-Fe) 30 and Zr 70 (Cu-Ni) 30 amorphous alloys. When the alloys annealed at temperatures below T g are heated, an excess endothermic reaction (enthalpy relaxation) occurs above the ...