In the case of the prWS2 layer, the estimated thickness was found to be 1.3 nm, with a mean mass density of 7.3 g/cm3. This result is close to the target thickness and to the density of a bulk WS2 monocrystal, which is 7.5 g/cm3. Figure 1. XRR diagrams of the prW and prWS2 ...