Theoretical considerations and test data indicate that, in the low-porosity range, the strength of set cement can be better predicted from its W hp *× G ... M Relis,I Soroka - 《Journal of the American Ceramic Society》 被引量: 2发表: 2010年 Compressive Strength Assessment of Soil-Ceme...
C109-水泥混凝土测试方法-Compressive Strength of Hydraulic Cement Mortar.pdf,Standard Method of Test f o r Compressive Strength of Hydraulic Cement Mortar a (Using 50-mm or 2-in. Cube Specimens) AASHTO DESIGNATION: T 106-00 (ASTM DESIGNATION: C 109K 109M-
Cement mortarRecycled asphalt pavementThis article presents the compressive strength and workability of cement mortar (CM) containing recycled asphalt pavement (RAP) as fine aggregate replacement. The effect of the RAP replacement, water to cement ratio, curing time, and aggregate water absorption on ...
To date, the most recommended compressive strength test procedure used for compressed earth blocks undertake direct, confined, tests on single units.References (30) P. Walker Strength, durability and shrinkage characteristics of cement stabilised soil blocks Cement Concrete Comp (1995) J.C. Morel et...
The compressive strength of cement is regarded as a principal indicator to determine the quality of cement. Therefore, efforts were focused to combine the factors which affect compressive strength together in such a form to develop suitable statistical models for predicting strength of cement at variou...
The compressive strength developing process and the microstructure of cement-asphalt mortar (CA mortar) were investigated. The fluidity of CA mortar has a great influence on its strength. The optimum value of spread diameter of slump flow test is in the range of 300 to 400 mm. The compressive...
The compressive strength is usually obtained experimentally by means of a compressive test where uniaxial compressive load is applied till its failure. Sobolkina et al. [19] investigated the dispersion of carbon nanotubes and its influence on the mechanical properties of the cement matrix with ...
For Low Heat Cement (LHC), its hydration reaction properties and compressive strength development were studied by quasi-elastic neutron scattering (QENS) and compressive strength test. In the QENS experiments, the amount of hydration products was estimated and the hydration behavior of LHC was reveale...
Unconfined compressive strength (UCS) of cement stabilized bases was collected from a number of highway construction projects in Thailand. Results from the statistical analysis indicated that the most important factors affecting the UCS were the CBR and the water to cement ratio. The UCS was however...
The cement shall be mixed with water to form a stiff paste and used within 2 h. (e) Special gypsum plasters Special high-strength gypsum plaster may be used to prepare a capping paste after being tested in the following manner: (i) The plaster-water mixture, prepared in the same ...