The research of CO 2 erosion-corrosion (E-C) of carbon steel pipelines in wet gas-solid flow, as a critical consideration for oil and gas engineering applications, is increasingly receiving more and more interest and attention. A semi-empirical model for the prediction and risk assessment of ...
[15] Barker R, Hua Y, Neville A.Internal corrosion of carbon steel pipelines for dense-phase CO2 transport in carbon capture and storage(CCS)- a review[J].International Materials Reviews, 2017,62(1):1-31. [16] 陈兵,康庆华,肖红亮.含杂质CO2管道输送泄漏扩散的数值模拟[J].安全与环境工程,20...
A106 grade B carbon steel, usually designed to be used as seamless pipe at high temperature and pressure, was used for corrosion testing in this work. The nominal chemical compositions (in weight percent) of A106 are 0.27 C, 0.26 Si, 0.86 Mn, 0.013 P, 0.022 S, 0.12 Cr, 0.04 Mo, 0.15...
Corrosion Behavior of Carbon Steel in the Monoethanolamine−H2O−CO2−O2−SO2 System: Products, Reaction Pathways, and Kinetics This work investigates the effect of operating parameters on corrosion products, reaction pathways, and kinetics for the corrosion of carbon steel in the m... N Klad...
The present study provides comprehensive information on the effects of process parameter variations on the corrosion behavior of carbon steel in CO2 absorption systems using aqueous amine solutions. The process parameters of interest are amine type, concentration of the amine solutions, solution temperature...
Prediction of CO2 corrosion of carbon steel 来自 ResearchGate 喜欢 0 阅读量: 546 作者:CD Waard,U Lotz 摘要: Starting from a 'worst case' corrosion rate prediction with the deWaard-Milliams equation, correction factors can be applied to quantify the influence of environmental parameters and ...
The corrosion rate of carbon steel in CO2 containing environments depends very much on the formation of protective corrosion product films. The parameters affecting film formation have been studied in a large number of flow loop experiments performed in the temperature range 20-120 C. Film formation...
Corrosion performance of carbon steel in CO_2 aqueous environment containing silty sand with different sizes was investigated by immersion tests and electrochemical measurements.Silty sand could form an adsorption layer on steel surface in initial period,and the sand adsorption layer was turned into a ...
In engineering design, corro- sion-resistant tube, protective layer tube, corrosion inhibitor, and cathodic protection are used to solve corrosion problem. KEY WORDS: carbon dioxide; pipeline transportation; CCUS; CO2 corrosion; corrosion control 收稿日期:2016-03- 18;修订日期:2016-05- 11 Received ...
Laboratory tests showed that properly welded X-60 pipeline steel was not susceptible to environmental failure in supercritical carbon dioxide (CO//2); and corrosion rates were less than 0. 02 mils penetration per year (MPY). Other tests showed nonmetallic seals to be susceptible to damage. Seals...