Jin L Z. The chloride stress - corrosion cracking behav- ior of stainless steels under different test methods [ J ]. Journal of Materials Engineering and Performance, 1994,3 (6) :734 - 739.L.Z.Jin, "The Chloride Stress-Corrosion Cracking Behaviour of Stainless Steels under Different Test ...
The cracking threshold of a 6Mo super austenitic stainless steel (UNS N08367) immersed in oxygen-bearing neutral chloride solutions is shown in Figure 3. The temperature thresholds are well above the 212°F (100°C) range, indicating that exposures to atmospheric boiling in neutral chloride solut...
stress corrosion crackingU-bendtemperature effectchloride concentrationsea saltThe Fe-21Cr-24Ni-6Mo UNS N08367 alloy was designed to be a seawater resistant alloy and has beenrnsuccessfully used in a multitude of marine and offshore applications including process piping systems,rnheat exchanger ...
This paper presents the effect of buffing on the stress corrosion cracking (SCC) resistance of machined surfaces of AISI 316L stainless steel (SS). Surface finishing operations are known to lower the SCC resistance of austenitic stainless steels and yet are unavoidable. AISI 316L SS samples were ...
Chloride stress corrosion cracking resistance of 6% Mo stainless steel alloy (UNS N08367)[J]. Desalination, 2001,135(1/3) :93 --97.James D. Fritz,Ronald J. Gerlock.Chloride stress corrosion cracking resistance of 6% Mo stainless steel alloy (UNS N08367)[J]. Desalination .2001(1)...
it must be carefully installed and bedded to ensure longitudinal cracking and overbelling does not occur. Additionally, PVC pipes can be fused together using various solvent cements, or heat-fused (butt-fusion process, similar to joining HDPE pipe), creating permanent joints that are virtually impe...
Production MethodsVinyl Chloride is produced by alkaline dehydrochlorination of ethylene dichloride, or by thermal cracking of EDC, or 1,1-dichloroethane. DefinitionChEBI: A monohaloethene that is ethene in which one of the hydrogens has been replaced by a chloro group. ...
While duplex stainless steels are considered resistant to stress corrosion cracking, they are not as resistant to this form of erosion as ferritic stainless steels. However, the least corrosion resistant duplex stainless steels have greater corrosion resistance than...
, Creep and stress corrosion cracking of austenitic stainless steel in boiling 35% magnesium chloride solution, Covos . Sci . , 1979, 19: 1019.M.Smialowski and J.Kostansking, Creep and stress corro- sion cracking of austenitic stainless steel in billing 35% magnesium chloride solution [J],...
Atmospheric stress corrosion cracking of austenitic stainless steel under limited chloride supply The occurrence of Atmospheric-Induced chloride Stress Corrosion Cracking in types 304L and 316L stainless steels contacted with sea-salt and magnesium chloride deposits has been studied under controlled conditions...