Herein, mesoporous Zn-doped g-C3N4 wrapped CdIn2S4 microsphere nanostructures were fabricated using a simple hydrothermal route. It is found that the CdIn2S4/Zn–g-C3N4 nanocomposite exhibits the most efficient photocatalytic activity for hydrogen evolution. The photocatalytic activity of the CdIn2S4/...
mpg-C3N4-catalyzed selective oxidation of alcohols using O2 and visible light. J. Am. Chem. Soc. 132, 16299–16301 Scientific Reports | 7: 27 | DOI:10.1038/s41598-017-00055-5 14 www.nature.com/scientificreports/ 16. Zhang, Y. H., Zhang, N., Tang, Z. R. & Xu, Y. J. ...
本发明公开了一种CdIn2S4/gC3N4复合光催化剂的制备方法及其应用.首先将gC3N4倒入50~100 mL醇中,gC3N4的浓度为5~10 g/L,然后超声浴30~50 min,以获得均匀的gC3N4分散体,得到溶液A;然后将一定量的CdIn2S4,加入溶液A中,继续超声处理30~50 min,CdIn2S4与gC3N4的质量比为3~12:100,得到溶液B;将溶液B在通风...
制备方法为:(1)通过煅烧法合成单体gC3N4,通过水热法合成单体CdIn2S4;(2)制备二元催化剂CdIn2S4/gC3N4;(3)制备三元催化剂Fe3+/CdIn2S4/gC3N4.所得三元光芬顿催化剂能用于在可见光条件下降解有机污染物.本发明通过简单绿色的湿式浸渍煅烧法合成三元催化剂Fe3+/CdIn2S4/gC3N4,该方法操作相对简单,反应条件相对...
After 120 min of irradiation by visible light, the photocatalytic efficiency of MO degradation of 7CIS/CN was 3.13 times higher than that of g-C3N4. When 60 mM H2O2 was added on this basis, the photocatalytic efficiency increased from 93.81 to 99.40%. The improvement of photocatalytic activity...
A dual mode immunosensing platform constructed on CdIn2S4 near-infrared electrochemiluminescence emitter and AuNPs@g-C3N4 for zearalenone sensingdoi:10.1016/j.microc.2024.111166CdIn2S4Dual-modeElectrochemical impedance spectroscopyElectrochemiluminescence
CdIn2S4/g-C3N4 heterojunction photocatalysts: enhanced photocatalytic performance and charge transfer mechanismdoi:10.1039/C6RA24809HDi LiFenfen ShiDeli JiangMin ChenWeidong ShiThe Royal Society of ChemistryLi, D.; Shi, F.; Jiang, D.; Chen, M.; Shi, W. CdIn2S4/g-C3N4 heterojunction ...
CdIn2S4/self-assembled g-C3N4 composite material with boosted photocatalytic degradation performance: The significance of morphology and structureGraphitic carbon nitrideSelf-assemblyMorphologyCadmium indium sulfidePhotocatalytic degradationElectron flowThe influence of morphology on the photocatalytic performance of ...
CdIn2S4/ g-C3N4 heterojunctionRedox capabilityHg2+Visible-lightThis investigation aims to prepare Z-scheme mesoporous CdIn 2 S 4 /g-C 3 N 4 heterojunction of reinforced photocatalytic efficiency appropriating the facile route of preparation. The synthetic procedure was adjusted such that the freshly...
The g-C3N4 nanosheets containing impurity levels (boron doping (BCN)) were prepared by a high-temperature solid-state reaction. Additionally, by anchoring the 3D dichalco-genide structures (CdIn2S4) elicited by a wet chemical route, hybrid BCN/CdIn2S4 nanostructures were obtained. The resulting...