(1982), "Caustic stress corrosion cracking of mild steel", Metallurgical Transaction A, Vol. 13A, pp. 1091-1098.Singbeil Y,Tromans L.Caustic stress corrosion cracking of mild steel. Metallurgical and Materials Transactions . 1982Singbeil Y,Tromans L.Caustic stress corrosion cracking of mild ...
corrosionphosphorus, Piron, FeThis paper reports on a study of the role of phosphorus in the caustic stress corrosion cracking of Ni Cr Mo V and Ni Cr V steels. The study was performed by carrying out constant load stress corrosion tests on smooth bar tensile samples for fixed lengths of ...
Investigations showed that caustic stress corrosion cracking (CSCC) was the predominant mechanism of cracking and failure of the tube. Misuse of boiler feed water, as the supplying water through the attemperator to the superheated steam, in the secondary superheater, and carryover from the steam ...
Caustic cracking is a form of stress corrosion cracking most frequently encountered in carbon steels or iron-chromium-nickel alloys that are exposed to concentrated hydroxide solutions at temperatures of 482°F (250°C). This phenomenon mostly occurs in boilers where caustic soda (NaOH) has been a...
In this way these impurities can lead to stress corrosion cracking (SCC) on stressed tubes of the steam generator. Such impurities can be strong alkaline or acid solutions. To evaluate the effect of alkaline concentrated environments on SCC of steam generator tubes, the tests were conducted on ...
Stress corrosion cracking of a commercial 0.19 pct C steel (SA-516 Grade 70) was studied in hot (92 C) caustic solutions of NaOH and NaOH plus aluminate (AlO 2 ) species. Potentiostatically controlled tests were conducted near the active-passive transition, using fracture mechanics testing tech...
6) alkali stress corrosion cracking 碱应力腐蚀开裂补充资料:穿晶开裂 分子式:CAS号:性质:金属材料开裂的金属学特征之一。裂纹由晶粒内部穿过。延性断裂的断口微观特征一般为韧窝状,脆性断裂的特征为解理或准解理花样。 说明:补充资料仅用于学习参考,请勿用于其它任何用途。
Stress corrosion cracking, possibly caustic cracking, is shown to occur on precracked specimens of cold drawn pearlitic eutectoid steel at room temperature, in the absence of applied potential, at pH values greater than 14.doi:10.1179/000705982798274642...
Stress corrosion cracking of a commercial 0.19 pct C steel (SA-516 Grade 70) was studied in hot (92 C) caustic solutions of NaOH and NaOH plus aluminate (A... ZY Wei - 《Scripta Metallurgica Et Materialia》 被引量: 1发表: 1994年 INVESTIGATION OF THE POTENTIAL FOR CAUSTIC STRESS CORROSI...