Density:2.67g/cm3 Linear density:430tex Fiber diameter:11μm Tensile strength:>2000Mpa Elastic modulus:>90GPa Elongation:2.2% OTHER MODELS PROVIDED: ModelFiber Diameter(μm)Linear Density(tex) XGBS9-87987 XGBS9-5249524 XGBS10-951095 XGBS10-80010800 ...
Density: 2.67g/cm3 Linear density: 2400tex Fiber diameter: 17μm Tensile strength: >2000Mpa Elastic modulus: >90GPa Elongation: 2.2% OTHER MODELS PROVIDED: Model Fiber Diameter(μm) Linear Density(tex) XGBS9-87 9 87 XGBS9-524 9 524 XGBS10-95 10 95 XGBS10-800 10 800 XGBS11-105 11...
Fiber density(tex))300±5% Weitght(g/m2)600g±5% +45 density(Root/cm)4.33±5% -45 density (Root/cm)4.33±5% Tensile strength(Laminate)Mpa>160 Standard width (mm)1270 Other weight specifications (customizable)350g,450g,800g,1000g
Fiber Appearance Continous Fiber Fiber Characteristics Continuous Basalt Fiber Diameter of Filaments 16um Glass Composition Basalt Fiber Filament Diameter 16um Package 10kgs/Roll Linear Density 1200/1600/200/2400/4800tex Color Golden Brown Transport Package Pallet Wrappe...
Density 2.7g/Cm Function Strengthen Certification ISO Trademark Leade Transport Package Bag Specification 16UM Origin China Product Description DESCRIPTIONChopped Basalt fiber is a product made continuous basalt fiber strands. The surface of the fiber coated with silane wetting agent. T...
Type BFRP Basalt fiber rebar Diameter (mm) 4~40 Density (g/cm3) 1.6~1.8 Tensile Strength (MPa) 1800 E-modulus (GPa) 140~155 Elongation (%) 1.3~1.5 coefficient of thermal expansion(×10-6/°C) 0 Application Related products Glass fiber rebar Basalt fiber rebar Company Profil...
1. Use carbon fiber and epoxy resin, light weight and high strength. 2. All-thread surface with good bond strength for concrete. 3. With excellent durability and corrosion resistance 4. Convenient for handle, reduce structure weight. Technical Data Type CFRP Diameter (mm)...
Fiber Diameter(μm) Average 16 Specific Area(M2/g) Approximate:2.6M2/g Color Yellow Brown Hardness 6Moh Melt point(ºC) >1450 Density(g/Cm) 2.7±0.25FUNCTIONReinforcing concrete beams with basalt fiber can defer the oblique cracks and restrain the development of ...
The specific resistance of basalt fiber (its density determines its breaking stress) is much higher than that of steel fibers. The basalt density is only 5% higher than that of the glass, and the tensile modulus of the basalt is higher than that of glass fiber. This makes basalt fiber the...
2. This chopped glass fiber has good fluidity, bundleability and small linear density, so there is no pilling and fluffing in mixing, and can be fully mixed with thermoplastic resin. It is widely used to reinforce PA, PP, PVC, ABAS, PC, etc.3. Fiberglass chopped strands also can ...