Bao-Wierzbicki (BW) damage modelContinuum damage mechanics (CDM)Sheet metal forming processesPositive stress triaxialityForming limit diagram (FLD)Damage growth phenomenon in sheet metal forming processes is one of the most important issues in the manufacturing industries. Predicting the onset and ...
Predicting ballistic impact failure of aluminium 6061-T6 with the rate-independent Bao-Wierzbicki fracture model. Int J Impact Eng 2015;76:207-20.A. Gilioli, A. Manes, M. Giglio, and T. Wierzbicki, "Predicting ballistic impact failure of aluminium 6061-T6 with the rate- independent Bao-...
The calibration of a Hosford–Coulomb fracture initiation model suggests that the ductility of aluminum 2024-T351 decreases monotonically as a function of the stress triaxiality, whereas it is a non-symmetric convex function of the Lode angle parameter. It is shown that a simple non-linear damage...
Predicting ballistic impact failure of aluminium 6061-T6 with the rate-independent Bao-Wierzbicki fracture model. Int J Impact Eng 2015;76:207-20.A. Gilioli, A. Manes, M. Giglio, and T. Wierzbicki, "Predicting ballistic impact failure of aluminium 6061-T6 with the rate- independent Bao-...