Materials and CorrosionE. Almeida, M. Morcillo and B. Rosales, "Atmospheric corrosion of mild steel Part II: marine atmospheres", Mater. Corros., Vol. 51(12), pp. 865-874, 2000.E. Almeida, M. Morcillo, and B. Rosales, "Atmospheric corro- sion of mild steel Part II--Marine ...
Atmospheric corrosion of mild steel. Part II – Marine atmospheres This paper summarizes the results obtained in the MICAT project for mild steel specimens exposed for 1 to 4 years in 47 marine atmospheres in the Ibero-American region. All these atmospheres were characterized for climatology, ...
This work analyses the corrosion mechanisms of carbon steel when exposed to marine atmospheres with very different chloride ion deposition rates. Two extre... D.,de,la,... - 《Materials & Corrosion》 被引量: 4发表: 2015年 Kinetics of atmospheric corrosion of mild steel in marine and rural ...
A great deal of information is available on the atmospheric corrosion of mild steel in the short, mid and even long term, but studies of the structure and morphology of corrosion layers are less abundant and generally deal with those formed in just a few years. The present study assesses the...
atmospheric corrosionlong term corrosionmild steelwettingdryingprotective rust layers/ A8160B Surface treatment and degradation of metals and alloys/ Fe/sur C /sur Fe/ss C/ssIn this paper an anomalous form of long term corrosion behaviour observed in mild steel exposed to some atmospheres in ...
The corrosion behavior of mild steel and Cr-containing steel has been investigated during wet/dry transitions. The corrosion potential was measured with a ... T Kamimura,M Stratmann - 《Corrosion Science》 被引量: 247发表: 2001年 Eight-Year Atmospheric Corrosion Exposure of Steels in China Atmos...
An Electrochemical Study of the Atmospheric Corrosion of Mild Steel .1. Experimental Method In this review the physico-chemical fundamentals of the atmospheric corrosion of iron are discussed, as they result from a number of electrochemical and sp... A Cox,SB Lyon 被引量: 75发表: 1994年 A ...
of the corrosion resistance of the 5 steels is as follow: 06CuP,CortenA,09CuP,20Steel,A3.The corrosion rate of A3 steel was 2.49 times higher than 06CuP which was the most corrosion resistant among the 5 steels.The weigh loss of the 5 steels all followed exponential decay function: Y=...
Corrosion rate of mild-steel, aluminium and zinc as well as the sulphation rate have been determined under outdoor exposure at Baroda (Petrochemical Complex Area, Central Gujarat) representing an industrial atmosphere. Monthly corrosion rate of mild-steel (MS), zinc and aluminium vary from 145.6 ...
Atmospheric corrosion of mild steel. Part II - Marine atmospheres The effects of Cl ion concentration and relative humidity on atmospheric corrosion behaviour of PCB-Cu under adsorbed thin electrolyte layer were investig... Almeida,E.,Morcillo,... - 《Materials & Corrosion》 被引量: 82发表: 200...