首先,ASTM B733标准明确了电镀的目的和适用范围,其目的在 于表面处理,增加特定的物理、化学或电学性质,例如耐磨、耐腐蚀、导电等,可应用于金属制品、塑料制品等表面的处理。 其次,ASTM B733制定了适用条件和限制。例如,电镀材料会影 响电缆和其他电气设备的机械和电学性能,因此根据镀层的厚度和铜 和钢之间的接触面...
Electrolessnickel is a hard coating that provides corrosion protection, wear resistance, and consistent thickness.ASTM B 733 Electrolytic Nickel Electrolytic nickel is a hard coating that provides corrosion protection; wear resistance, and bright finish.ASTM B 689 Electrodeposited Tin Electrodeposited Tin ...
内容提示: ASTM B733-2015金属上自动催化(无电镀)镍-磷 磷涂层标准规范Standard Specification for Autocatalytic (Electroless)Nickel-Phosphorus Coatings on Metal 文档格式:PDF | 页数:24 | 浏览次数:1000 | 上传日期:2017-06-16 11:47:28 | 文档星级: ASTM B733-2015金属上自动催化(无电镀)镍-磷 磷...
ASTM B733-04由美国材料与试验协会 US-ASTM 发布于 2004。 ASTM B733-04 在中国标准分类中归属于: A29 材料防护。 ASTM B733-04 金属表面自催化(无电)镍磷涂层标准规范的最新版本是哪一版? 1.1 本规范涵盖了从水溶液到工程(功能)用途的金属产品的自催化(化学镀)镍磷涂层的要求。 1.2 该涂层是通过次磷酸...
116 p. API SPEC 5B-2017 -油管、套管和管线管螺纹的加工、测量和检验 中英文 13 p. ASTM A193-A193M-2001 中文版 合金钢及不锈钢栓接材料(冲突时的文件备份2013-08-27 19-55-42) 190 p. ASME B16.34 44 p. ASME B16.9-2001 18 p. MSS SP-55-2001(英文版) 关于...
Designation: B 733 – 97 Standard Specication for Autocatalytic (Electroless) Nickel-Phosphorus Coatings on Metal 1 This standard is issued under the xed designation B 733; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the ...
ASTM B733-22 引用标准 ASTM B368ASTM B374ASTM B380ASTM B487ASTM B499ASTM B504ASTM B537ASTM B567ASTM B568ASTM B571ASTM B578ASTM B602ASTM B667ASTM B678ASTM B697ASTM B762ASTM B849ASTM B850ASTM B851ASTM D1193ASTM D2670ASTM D2714ASTM D3951ASTM D4060ASTM E140ASTM E156ASTM E352ASTM E60...
现在位置: astm b733中文版astm b733中文版astmb733电镀标准 首先,ASTM B733标准明确了电镀的目的和适用范围,其目的在 于表面处理,增...ASTM B-733-97 金属表面化学镀镍磷层规范标准 ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States. 1 B 733 ...
Designation: B733 − 15Standard Specif i cation forAutocatalytic (Electroless) Nickel-Phosphorus Coatings onMetal1This standard is issued under the f i xed designation B733; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the ye...
3 B 733 – 97 6.3 Stress Relief: 6.3.1 Pretreatment of Iron and Steel for Reducing the Risk of Hydrogen Embrittlement—Parts that are made of steel with ultimate tensile strength of greater than 1000 Mpa (hardness of 31 HRC or greater), that have been machined, ground, cold formed, or ...