Designation: A565/A565M – 10Standard Specif i cation forMartensitic Stainless Steel Bars for High-TemperatureService 1This standard is issued under the f i xed designation A565/A565M; the number immediately following the designation indicates the yearof original adoption or, in the case of rev...
同时，随着新材料、新技术的不断涌现，未来ASTM A565/A565M标准还将继续发展，以满足更加复杂和多样化的工业应用需求。总之，ASTM A565/A565M-05a(2009)标准作为高温用马氏体不锈钢棒材的重要规范，其制定和实施对于保障工业设备的安全运行、提高生产效率和降低维护成本具有重要意义。随着标准的不断更新和完善，我们...
Designation: A565/A565M − 10 (Reapproved 2017) ´1Standard Specif i cation forMartensitic Stainless Steel Bars for High-TemperatureService 1This standard is issued under the f i xed designation A565/A565M; the number immediately following the designation indicates the yearof original adoption...
ASTM A565 Gr.616HT化学成分 C (%): 0.20 ~ 0.25 Si (%):≤ 0.75 Mn (%):≤ 1.00 P (%)≤:0.030 S (%)≤:0.015 Cr (%): 11.5 ~ 13.5 Ni (%):0.50 ~ 1.00 Mo (%): 0.95 ~ 1.25 V (%): 0.15 ~ 0.30 W (%): 0.95 ~ 1.25 上海隆继金属集团有限公司优势特点: 1、强大的价格优势...
对应标准ASTM A565/A565M-2010(R2017) 高温用马氏体不锈钢棒 Martensitic Stainless Steel Bars for High-Temperature Service 归类马氏体不锈钢 化学元素成分含量(%) 成分CSiMnPSCrNiCuMoN 最小值--0.5--124-1.50.06 最大值0.050.510.020.0051570.320.12 ...
对应标准ASTM A565/A565M-2010(R2017) 高温用马氏体不锈钢棒 Martensitic Stainless Steel Bars for High-Temperature Service 归类马氏体不锈钢 XM-32 化学元素成分含量(%) 成分CSiMnPSCrNiMoNV 最小值0.08-0.5--1121.50.010.25 最大值0.150.350.90.0250.02512.5320.050.4 ...
首頁/ 產品與标準/ ASTM A565/A565M - 2010 (R2017) 高溫用馬氏體不鏽鋼棒[材料] 簡體 繁體 高溫用馬氏體不鏽鋼棒 ASTM A565/A565M - 2010 (R2017) 牌号 美國UNS S41041 美國UNS S41425 美國UNS S42226 牌号 615 美國UNS S41800
ASTM A565 XM-32不锈钢热处理工艺的研究
ASTM A565-2009 Martensitic Stainless Steel Bars Designation:A565/A565M–05a(Reapproved2009)Standard Specification for Martensitic Stainless Steel Bars for High-Temperature Service1 This standard is issued under thefixed designation A565/A565M;the number immediately following the designation indicates...
ASTM A565/A565M标准SUH616与AISI422力学性能 SUH616属于日标耐热钢,执行标准:JIS G4311-1991 SUH616耐热钢,日本JIS标准马氏体系列耐热钢。SUH616就是422的别名,是在11～l3%Cr的钢中加入MO、W、V、Ni等,在650℃以下高温强度大的合 金。AISI规定为616,用于高温螺栓、螺母、汽轮机叶片等。SUH616对应中国GB 2...