ASTM A1016/A1016M-17a, ASTM A1016/A1016M-17, ASTM A1016/A1016M-14e1, ASTM A1016/A1016M-14, ASTM A1016/A1016M-13, ASTM A1016/A1016M-11a, ASTM A1016/A1016M-11, ASTM A1016/A1016M-10, ASTM A1016/A1016M-08, ASTM A1016/A1016M-04a, ASTM A1016/A1016M-04, ASTM...
11.1.7.3.2Thefaceshallbepolishedpracticallyfreeofscratches 6.3.6IftheresultsofthemechanicaltestsofanyGradeUandshallbeetchedtodefinethemicrostructure.Thespecimen lotofaxlesdonotconformtotherequirementsspecified,theshallbeexaminedunderamagnificationof100diameters. axlehavingtheprolongationfromwhichthetensionspec...
ASTM A1016/A1016M - 13 Standard Specification for General Requirements for Ferritic Alloy Steel, Austenitic Alloy Steel, and Stainless Steel Tubes - See all versionsASTM A1017/A1017M - 11 Standard Specification for Pressure Vessel Plates, Alloy Steel, Chromium-Molybdenum-Tungsten - See all ...
(Section 16), and where the analysis is not sufficiently complete to permit 3.1.21 Straightness Test Method (see 8.5 and 9.6). conformance to be determined, the chemical composition determined from a product analysis made by the tubular 4. Materials and Manufacture manufacturer shall conform to ...
free of visible pipe and conditioned as necessary to remove injurious surface imperfections 7 Certifi cation and Test Reports 7 1 When specifi ed by the purchaser a manufacturer s certifi cation that the material was manufactured and tested in accordance with this specifi cation together with a ...
All tubes shall be free of excessive mill scale, suitable for inspection. A slight amount of oxidation will not be considered as scale. Any special finish requirements shall be subject to agreement between the manufacturer and the purchaser. ...
4.1.2 Weld repairs, with the addition of compatible ller metal, may be made to the weld joint in accordance with the requirements of the section on Repair by Welding of Specication A 999/A 999M. 4.1.3 The pipe shall be pickled free of scale. When bright annealing is used, pickling ...
The outside and inside surfaces of the tubes shall be free of loose scale, metallic particles, or other material which would tend to restrict signals or create electrical noise. The tubing shall be inspected by feeding it longitudinally through an inspection coil or coils with a diameter ...
4.4.2 Springs with ground ends having a free height-tomean diameter ratio of not less than 1 or more than 5 shall not deviate from the perpendicular more than the number of degrees prescribed in Table 3, as determined by standing the spring on its end and measuring the angular deviation ...
A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (´) indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specif i cation covers styrene monomer.1.2 The following appli......