The physical properties of the Aluminum / Aluminium 3003 alloy are tabulated below.PropertiesMetricImperial Density 2.73 g/cm3 0.0939 lb/in3 Melting point 644°C 1190°FMechanical PropertiesThe mechanical properties of the Aluminum / Aluminium 3003 alloy are outlined in the following table....
Chemical Composition Limits Weight% Al Cu Si Fe Mn Zn Others Alloy 3003 Rem 0.05-0.20 0.60 max 0.70 max 1.0-1.5 0.10 max 0.05 each 0.15 totalTypical Mechanical PropertiesMaterial Condition Tensile Strength (ksi min) Yield Strength (ksi min) Elongation % in 2" 0.064 Sheet Min 90° Cold ...
The AA3003 aluminium alloy was deformed by isothermal compression in the deformation temperature range 300-500 degrees C at a strain rate of 0.1 s(-1) with a Gleeble-1500 thermal simulator. The microstructure of the alloy was observed by OM and TEM, and the hardness was measured with a ...
Mechanical Properties of Aluminium Circle Temper Thickness(mm) Tensile Strength Elongation Standard HO 0.36-5 60-100 ≥ 20 GB/T91-2002 H12 0.5-5 70-120 ≥ 4 H14 0.5-5 85-120 ≥ 2 Chemical Compositions Alloy Min.AL Si Fe Cu Mn Mg Ni Zn V Other 1050 99.5 0.25 0.4 0.05 0.05...
(slightly higher than that of industrial pure aluminum), and it cannot be strengthened by heat treatment. Therefore, cold working method is adopted to improve its mechanical properties:In the annealing state has a high plasticity, in the semi-cold hardening plastic...
Chemical Composition (based on alloy 3003): Element Actual Value Element Actual Value Al Rest Si 0.134 Fe 0.489 Cu 0.1 Mn 1.07 Mg 0.0058 Cr 0.0039 Ni 0.005 Zn 0.005 Ti 0.03 Mechanical Properties (based on alloy 3003) Property Test result Yield Strength 150MPa Tensile Strength 155MPa ...
Chemical Composition (based on alloy 3003): Element Actual Value Element Actual Value Al Rest Si 0.134 Fe 0.489 Cu 0.1 Mn 1.07 Mg 0.0058 Cr 0.0039 Ni 0.005 Zn 0.005 Ti 0.03 Mechanical Properties (based on alloy 3003) Property Test result Yield Strength 150MPa Tensile Strength 1...
3003 aluminum sheets/coils belong to a kind of AL-Mn alloy which is approximately 10% stronger than alloy 1100. 3003 aluminum sheets are non-heat treatable, so the mechanical property is improved by cold processing: it has high plasticity in annealed condition, good plasticity when sem...
Mechanical Properties Tensile Strength(U.T.S): 35 MPA - 100 MPA Elongation≥0.5% Standard ASTMB209,EN573-1S Packaging Seaworthy Export Standard Wooden Box Application Cigarette Packaging, Lamination and Food Packaging Production process Product t...
Good mechanical properties and forming performance.Our products have perfect flatness, clean and clear surface with uniform color. Flexible packaging aluminum foilApplication:food packaging bags, packaging paper, cooking bagsAlloy: 1235, 8079Temper:HOThickness:0.006mm-0.2mmWid...