Phase Diagrams and Physical Properties of Nonequilibrium AlloysNonequilibrium Phase Diagrams of Ternary Amorphous AlloysSummary This document is part of Subvolume A 'Nonequilibrium Phase Diagrams of Ternary Amorphous Alloys' of Volume 37 'Phase Diagrams and Physical Properties of Nonequilibrium Alloys' ...
第六章低Cu的Al-Zn合金中亚稳相转变引起的组织异常细化 (89)6.1 AlZn-2Cu合金退火后的相组成与组织 (90)6.2 AlZn-2Cu合金冷变形后的相组成与组织 (92)6.3 AlZn-2Cu合金组织的异常细化 (93)6.4 小结 (97)本章参考文献 (99)第七章结论 (101)攻博期间发表论文 (103)致谢 (105)作者简历 ...
and the structure of Al 37 Zn 1 Mg 2 was the most stable.Key words phase diagram, second phases, solid solutions, formation enthalpy, cohesive energy, intrinsic properties0 引言Al-Zn-Mg 系(7xxx 系)铝合金是一种可热处理强化的高强度铝合金,具有高的比强度和比模量、优良的焊接性能、良好的机械...
The room temperature phase diagram of Al-Zn-Cu system is the important basis for judging the phase constituents of the materials at the usage condition. New results about the room temperature phase diagram of the low copper side in the Al-Zn-Cu systems have been shown in this study. Miscibi...
Al系平衡相图。常用的两种Zn2Al二元相图 [1,2] ,除了 特殊点线的成分和温度稍有差别外,两者最大的区别在 于是否存在β(ZnAl)固溶单相区,是否存在β(ZnAl) 相。本课题利用高温X射线衍射法(XRD)、示差扫描 量热分析法(DSC)、热膨胀法(PRD)等方法重新测定部 ...
The thermodynamics of instability of the cc-solid solution in Al-Zn alloys was studied on the basis of the Gibbs-Duhem equation of chemical potentials in a solution and including the energy of transition of an hexagonal lattice into a fee one. The Al-Zn phase diagram which shows the dependen...
Al_Zn_Cu三元系低Cu侧相平衡_相变与扩散的研究_21_25 东北大学博士学位论文第一章绪论 功的应用。并于1977年创办了以考夫曼为主编的国际性学术杂志[51]：CALPHAD (Computer Coupling of Phase diagram & Thermochemistry)，从1970年起每年召开一次国际学术会议，不仅大大促进了热力学计算相图的发展，而且对整个相图...
phasediagram;AI.Zn.Si.Mgsystem;hot—dip;alloying;anticorrosionperformance Al-Zn-Si-Mg四元相图计算在铝锌镀层合金化研究的应用作者: 赵阳子, 李谦, 陈双林, 张捷宇, 周国治作者单位: 赵阳子,李谦,张捷宇(上海大学大学材料科学与工程学院,上海 200072), 陈双林(上海大学大学材料科学与工程学院,上海 200072 ...
合金演变组织ternaryphase三元 关键词:相图等温截面ALZ卜La三元合金系Cu_Ti—Er三元合金系X射线衍射分析Cu.Ti二元合金系组织演变木本论文得到国家自然科学基金项目(50831007)资助Ⅱ TERNARYPHASEDIAGRAMoFTHEAL__ZR—LAANDCU—-TI._】ERANDMICROSTRUCTURALCHARACTERIZATIoNoFCU—-TIALLOYSABSTRACTThephaserelationsintheA卜Z卜...
Al-Mg-Ce、Al-Mg-Zr和Al-Mg-Sc-Zn体系的相平衡、热力学模拟及应用 CALPHAD (CALculation of PHAse Diagram)技术广泛成功应用于多组元体系的相图热力学计算。CALPHAD方法成功的关键在于选用合理的模型以及准确的相图热力学数据。本工作... 李茜 - 中南大学 被引量: 0发表: 2015年 L12相强化的耐热铝合金相关体系...