The corrosion behavior of low carbon steel (AISI 1010) is strongly influenced by grain size variations, which in turn affect the microstructural mechanical properties of the material. The mechanical behavior and performance of metallic materials, including their corrosion resistance, is determined by ...
Mechanical Properties The mechanical properties of AISI 1010 cold drawn carbon steel are tabulated below. PropertiesMetricImperial Tensile strength365 MPa52900 psi Yield strength (depending on temper)305 MPa44200 psi Elastic modulus190-210 Gpa27557-30458 ksi ...
0.284 lb/in?/font> Mechanical Properties Hardness, Brinell 105105 Hardness, Knoop 123 123 Converted from Brinell hardness.Hardness, Rockwell B 6060 Converted from Brinell hardness.Hardness, Vickers 108108 Converted from Brinell hardness.Tensile Strength, Ultimate 365 MPa 52900 psi Tensile Strength, ...
1010 1015 %C 0.08 - 0.13 0.12 - 0.18 %Si 0.10 - 0.35 0.10 - 0.35 %Mn 0.30 - 0.60 0.30 - 0.60 %P 0.040 Max 0.040 Max %S 0.050 Max 0.050 Max 3-Mechanical Properties Soft Hardened Density 7.82 g/cm3 7.82 g/m3 Hardness 60 - 90 HRB 55 - 60 HRC Tensile ...
AISI 1018 low carbon steel offers a good balance of toughness, strength and ductility which is the most commonly available grade around the world.Although its mechanical properties are not very unique, it still can be easily formed, machined, welded and
Boiler and pressure vessel steel Q/BQB 320 HII DIN 17155 (EN10028-2) HII (P265GH) In addition to ensuring normal temperature performance, it also guarantees mechanical properties at higher temperatures, and is suitable ...
H13 Steel Properties High hot-wear resistance and hot tensile strength as well as good toughness, thermal conductivity and insusceptibility to hotcracking. Can be water-cooled to a limited extent. Mechanical Properties: Tensile strength 1550 MPa-2050MPa Yield Strength 1000-1380 MPa Elongation 10%-...
AISI H13 Steel Properties High hot-wear resistance and hot tensile strength as well as good toughness, thermal conductivity and insusceptibility to hotcracking. Can be water-cooled to a limited extent. Mechanical Properties: Tensile strength 1550 MPa-2050MPa Yield Strength 1000-1380 MPa Elongation...
Feature:feature with high toughness,good corrosion resistance and remarkable mechanical properties at high and low temperature. Medical application: chemical pump,valve,petrochemical,nuclear power,high-end cosmetics,Medical eqipment,body ...
Mechanical Property Hardness HRC Tensile Strength (Rm) Mpa Yield Strength (RP0.2) Mpa 44 1400 1150 48 1620 1380 Heat Treatment Soft Annealing Heating steels upto 850ºC in protective atmosphere; after soaking, then have cooling in the furnace at the rate of 10ºC/hr; after tem...