STM A564-630是一种马氏体沉淀硬化铬镍铜不锈钢。ASTM A564-630钢可以通过在相对较低的温度下进行一次时效处理来硬化,从而将变形的风险降到很低。 不锈钢沉淀硬化钢17-4PH,17-4 PH,1.4542,X5CRNICUNB17-4-4,AISI 630,符合EN 10088-1,ASTM A564的UNS S17400。 17-4PH,X5CrNiCuNb16-4、1.4542,X5CrNiCu...
钢材 淬火和/或时效(H1150M):760°C保持2h,空冷+620°C保持4h,空冷 ≥795 ≥520 ≥18 ≥55 HRC: ≥24HB: ≥255 ≥75 钢材 淬火和/或时效(H1150D):620°C保持4h,空冷+620°C保持4h,空冷 ≥860 ≥725 ≥16 ≥50 HRC: 24~33HB: 255~311 ≥41 • 洛氏和布氏硬度都是允许的。尺寸12.7mm及...
incl 145 [1000] 125 [860] 13 45 32 311 20 27 4.0 air cool H1100 1100 [595] [200 mm] (L) 140 [965] 115 [795] 14 45 31 302 25 34 H1150 1150 [620] 135 [930] 105 [725] 16 50 28 277 30 41 1400 [760] for 2 h, air cool plus H1150M 115 [795] 75 [520] 18 55 ...
Types 630, XM-16, and XM-25 may be furnished in the solution-annealed or age-hardened condition. 5.1.2 Type UNS S46910 shall be furnished in solution- annealed condition in accordance with Table 2, or solution- annealed and cold-worked condition in accordance with Table 3, or aged-...
H1150M 1400 760 for 2 h air cool plus 1150 620 for 4 h air cool Up to 12 in incl 300 mm L 115 795 75 515 1855 24255 5575 Up to 12 in incl 300 mm T 14353547 XM 13 H950950 510 4 0air cool Up to 12 in incl 300 mm L 220 1515 205 1415 10 45 45430 Up to 12 in incl...