Incoloy® Alloy A286 is iron-nickel-chromium based austenitic iron based material that consist of molybdenum and titanium as an addition. Cres A286 alloy is known for its good strength and oxidation resistance especially at temperatures up to 1300°F (700°C). A286 is an age-hardenable iron-...
We are using the A286 screws in Jetfoil repairing. Now we are going to look for substitution. We just have the material chemical composition and physical...
Chemical Composition Limits Weight% C Mn P S Si Cr Ni Mo Ti V Al B Co Cu A286 0.08 max 2 max 0.025 max 0.025 max 1 max 13.5-16 24-27 1-1.5 1.9-2.35 0.10-0.50 0.35 max 0.0003-0.010 1 max 0.50 maxAlloy A286 bar can be solution treated at the temperatures detailed below, rapid...
We could supply A-286, UNS S66286, 1.4980 forging steel material certificate as per the standard of EN10204-3.1 or EN10204-3.2 of third party Our A-286, UNS S66286, 1.4980 forged/forging rings are widely used in chemical pump, centrifugal pumps, ball v...
A286 alloy is a heat and corrosion resistant austenitic ironbase material which can be age hardened to a high strength level. The alloy is also used for low temperature applications requiring a ductile, non-magnetic high strength material at temperatures ranging from above room temperature down to...
The chemical composition of the commercial A286 alloy used in this study is listed in Table 1. Samples of the material were obtained from a hot-rolled bar 12.5 mm in diameter. The specimens were solution treated for 1 h at 930 °C, air cooled and aged for 16 h at 730 °C to obtain...
Chemical Composition Grade C Si Mn P S Ni Cr Mo 201 ≤0.15 ≤0.75 5.5-7.5 ≤0.06 ≤ 0.03 3.5-5.5 16.0-18.0 - 301 ≤0.15 ≤1.0 ≤2.0 ≤0.045 ≤ 0.03 6.0-8.0 16.0-18.0 - 304 ≤0.08 ≤1.0 ≤2.0 ≤0.045 ...
chemical compositionchromium carbidesThe results of microstructural characterization and stress corrosion cracking tests are presented for several heat treatment conditions of the age-hardenable Alloys X750, 718, and A286. Resistance to intergranular stress corrosion cracking (IGSCC) was evaluated using slow...
Type A286 alloy can be produced by AOD refining or vacuum induction melting. Vacuum arc or electroslag remelting procedures may be used to further refine the material. Type A286 alloy is available in plate, sheet and strip.CHEMICAL COMPOSITION Typical Analysis Element Percent Carbon 0.08 max ...
Chemical Composition GradeCSiMnPSNiCrMo 201≤0.15≤0.755.5-7.5≤0.06≤ 0.033.5-5.516.0-18.0- 301≤0.15≤1.0≤2.0≤0.045≤ 0.036.0-8.016.0-18.0- 304≤0.08≤1.0≤2.0≤0.045≤ 0.038.0-10.518.0-20.0- 304L≤0.03≤1.0≤2.0≤0.035≤ 0.039.0-13.018.0-20.0- ...