物理特性(Physical Properties) 密度(Density):2.7g/cm3 机械性能(Mechanical Properties) 抗拉强度(强度极限)(Tensile Strength, Ultimate):290 MPa(42000psi) 屈服强度(屈服极限)(Tensile Stre…
机械性能分析(Typical Mechanical Properties) 铝合金牌号及状态 拉伸强度 屈服强度 硬度 延伸率 (25°C MPa) (25°C MPa) 500kg力10mm球 1.6mm(1/16in)厚度 ALLOY AND TEMPER Ultimate Tensile Strength Tensile Yield Strength Hardness Elongation 6061-T6 / 6061-T651 ...
Aluminum and its alloys are having variety of applications in today's industrial scenario. The use of Al and its alloys are increasing day by day due to its specific properties, like light weight, high strength, and excellent corrosion resistance. Present study is conducted on Aluminum 6061 ...
典型合金6061机械和物理性能(Typical Mechanical & Physical Properties) 焊接性 切削性 耐蚀性 电导率20℃(68℉)(%IACS) 密度(20℃)(g/cm3) 容易焊接 及好 很好 40-50 2.7 抗拉强度(MPa) 屈服强度(MPa) 硬度500kg力10mm球 延伸率1.6mm(1/16in)厚度 剪应力MPa 240 205 95 9 - 6061典型用途: 6061...
Mechanical properties 合金牌号铝合金牌号及 状态 抗拉强度 Rm/Mpa 屈服强度 Rp0.2/Mpa 延伸率/% 硬度/ HBWα 6061-T6 290 240 10 95 物理性能/ physical property 金牌号铝合金牌号及 状态 热膨胀系数 (20-100℃) μm/m·k Rm/Mpa 熔点范围 (℃) Rp0.2/Mpa 电导率 20℃(68℉) (%IACS) 电阻率...
铝合金的典型机械性能(Typical Mechanical Properties) 铝合号 及状态 拉伸强度(25°C MPa) 屈服强度(25°C MPa) 硬度500kg力10mm球 延伸率1.6mm(1/16in)厚度 5052-H112 175 195 60 12 5083-H112 180 211 65 14 6061-T651 310 276 95 12 7050-T7451 510 455 135 10 7075-T651 572 503 150 11 2024...
Niroumand, B.Taylor & FrancisScience and Technology of Welding & JoiningHajihashemi, M., Shamanian, M., and Niroumand, B., 2016, "Microstructure and mechanical properties of Al-6061-T6 alloy welded by a new hybrid FSW/SSW joining process," Sci. Technol. Weld. Join., 21(6), pp. ...
Laser welding is widely used for the joining of aluminum alloy in the automotive industry, and the vehicles produced are inevitably subjected to high strain rate loading during their service. Therefore, this paper studied the mechanical properties of 6061-T6 aluminum alloy and its ...
alloyandthesameseriesAl2alloyproducedinEurope.Usingacubic polynomial,theformulatodeterminethemechanicalpropertiesofAl2alloyatelevatedtemperaturesisdevelopedbyusing regressionoftestresults. Keywords:elevatedtemperatures;aluminium2alloy(Al2alloy);materi 君,已阅读到文档的结尾了呢~~...
The local mechanical properties of a weld zone, in a 6061-T6 aluminium alloy subjected to the modified indirect electric arc technique have been studied. The mechanical properties of the base metal, the weld metal and the heat affected zone were determined by means of usual and instrumented inde...