屈服强度(屈服极限)(Tensile Strength, Yield):255MPa(37000psi) 断裂延伸率(Elongation at Break):12%(@Thickness 1.59mm) 弹性模量(Modulus of Elasticity):68.9 GPa(10000ksi) 剪切强度(Shear Strength):186MPa(27000psi) 工艺性能(Processing Properties) 溶解温度(Solution Temperature ):529℃(985℉) 时效温度...
Clifton, Pressure-Shear Waves in 6061-T6 Aluminum and Al- pha-Titanium, J. Mech. Phys. Solids, Vol 33 (No.3), 1985, p 263-284A. Gilat and R. J. Clifton.Pressure-shear waves in 6061-T6 aluminum and alpha-titanium. Journal of the Mechanics and Physics of Solids . 1985...
356.0-T6 Cast Aluminum6061-T6 Aluminum Metric UnitsUS Customary Units Mechanical Properties Brinell Hardness75 93 Elastic (Young's, Tensile) Modulus, GPa70 69 Elongation at Break, %3.8 10 Fatigue Strength, MPa75 96 Poisson's Ratio0.33
MaterialData_AL 6061 T6 Tensile Strength, Ultimate Tensile Strength, Yield
Aluminum 6061-T6; 6061-T651 Subcategory: 6000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal Composition Notes: Aluminum content reported is calculated as remainder. Composition information provided by the Aluminum Association and is not for design. Key Words: al6061, UNS A96061; ...
Aluminum 6061-T6; 6061-T651 Categories: Metal; Nonferrous Metal; Aluminum Alloy; 6000 Series Aluminum Alloy Material Information provided by Alcoa, Starmet and the references. General 6061 characteristics and uses: Notes: Excellent joining characteristics, good acceptance of applied coatings. Combines ...
Shear strength 207 MPa 30000 psi Fatigue strength 96.5 MPa 14000 psi Elastic modulus 68.9 GPa 10000 ksi Poisson's ratio 0.33 0.33 Elongation 12-17% 12-17% Hardness, Brinell 95 95 Thermal Properties The thermal properties of Aluminium / Aluminum 6061 alloy are given in the following table. Pro...
al., "Dynamic shear band formation in Aluminum 6061-T6 and Aluminum 6061-T6/Al2O3 composites", Volume 457, Issues 1-2, 25 May 2007, Pages 114-119.G.M. Owolabi, A.G. Odeshi, M.N.K. Singh, M.N. Bassim, Dynamic shear band formation in aluminum 6061-T6 and aluminum 6061-T6/...
In the table below, I have tried to list the key mechanical properties for billet (bar) and forged material for both 7075-T6 and 6061-T6 aluminum alloys. The data listed should give you a good idea on the tensile, compressive, shear and bearing strengths of these materials. ...
ModulusofElasticity68.9GPa10000ksiAA;Typical;Averageoftensionandcompression.Compressionmodulusisabout2%greaterthantensilemodulus. ShearStrength186MPa27000psiAA;Typical ProcessingProperties SolutionTemperature529°C985°F AgingTemperature160°C320°FRolledordrawnproducts;holdattemperaturefor18hr ...