Aluminum Alloy, Sheet 1.0Mg - 0.8Si - 0.8Cu - 0.50Mn (6013-T6) Solution Heat Treated and Artificially Aged SAE AMS4216 发布历史 SAE AMS4216由美国机动车工程师协会 US-SAE 发布于 1989-07-01。 SAE AMS4216 铝合金 1.0Mg - 0.8Si-0.8Cu-0.50Mn(6013-T6)热处理和人工老化溶液的最新版本是哪一...
The company is mainly engaged in the business of imported aluminum, aluminum rod aluminum by the Alcoa Corp, the domestic high-quality aluminum alloy, copper alloy material, it is widely used in aerospace, transportation, machinery, mold, plastic products, electronic products, precision instruments,...
Aluminum Alloy, Sheet 1.0Mg - 0.8Si - 0.8Cu - 0.50Mn (6013-T6) Solution Heat Treated and Artificially Aged 点击打开全屏PDF预览 点击查看大图 标准号 SAE AMS4216C-2020 2020年 总页数 4页 发布单位 美国机动车工程师协会 当前最新 SAE AMS4216C-2020 ...
R Braun,C D Donne,G Staniek.Laser beam welding and friction stir welding of 6013-T6 aluminum alloy sheet. Materialwissenschaft und Werkstofftechnik . 2000Braun R, Donne CD, Staniek G. Laser beam welding and friction stir welding of 6013-T6 aluminium alloy sheet. Mat.-wiss.u.Werkstofftech J...
英文标准名称:Aluminum Alloy, Sheet 1.0Mg - 0.8Si - 0.8Cu - 0.50Mn (6013-T6) Solution Heat Treated and Artificially Aged UNS A96013 标准类型:V11 发布日期:2003/7/1 12:00:00 实施日期:1999/12/31 12:00:00 中国标准分类号:V11 国际标准分类号:49.025.20 ...
6xxx aluminum alloyscoarseningmechanical characterizationwarm sheet formingThe use of warm forming for AA6xxx-T6 sheet is of interest to improve its formability; however, the effect warm forming may have on the coarsening of precipitates and the mechanical strength of these......
Corrosion Behaviour of Dissimilar A319 and A356 Cast Aluminum Alloys Joined By Friction Stir Welding (FSW) In the present investigation, the corrosion behaviour of dissimilar A319 and A356 cast Al alloys plates joined by friction stir welding (FSW) was evaluated. The effects of tool rotational and...
Though this process can be accomplished with a variety of lasers, adhesives and substrates, this research focuses on laser weld bonding of 1.0 to 1.6-mm thick 6013-T6 aluminum alloy using a 5 kW fiber laser with Al 4047 filler wire and Hysol EA 9628 epoxy film adhesive. The intent of ...
RetrogressionHigh strengthAluminum formingThe kinetics of retrogression in a high-strength aluminum AA6013-T6 (Al-Mg-Cu-Si) sheet are investigated to determine retrogression heat treatments that allow subsequent reaging to approximately...doi:10.1007/978-3-030-05864-7_22Katherine E. Rader...
Aluminum Alloy, Sheet 1.0Mg - 0.8Si - 0.8Cu - 0.50Mn (6013-T6) Solution Heat Treated and Artificially Ageddoi:SAE AMS4216B本规范涵盖板材形式的铝合金.该板材通常用于要求具有良好强度,韧性,疲劳财产和最大耐腐蚀性的结构件,但其使用不限于此类应用....