34CrNiMo6工程钢的热处理 34CrNiMo6 钢的淬火和回火 (Q+T) 将34CrNiMo6圆钢缓慢加热至850的温度; 在此硬化温度下浸泡在油中淬火; 34CrNiMo6钢一达到室温就回火。 均匀加热至合适温度; 从炉中取出并在空气中冷却。 通常回火温度为600C,具体温度根据实际要求而定。 DIN 34CrNiMo6 / 1.6582 钢锻造 热成型温度:1100...
二、机械性能试验(调至处理后)(参照标准:EN 10083-3--2006)Mechanical performance test(Q+T) 检测项目Test items 标准值Standardvalue 实测结果Experimental results 判定Determine 抗拉强度Tensile strength(MPa) 1000--1200 1176 合格OK 屈服点Yield point(MPa) ≥800 912 合格OK 断后伸长率Elongation(%) ≥11 ...
Tempering +T 540-680oC In air Heat Treatment Guide generated Graphs The following graphs are generated from a theoretical model. For further info see the Heat treatment guide module. Select a specific grade version for individual display. 1002003004005006007000100200300400500600 356D 34CrNiMo6356Q 34CrN...
34CrNiMo6、25Cr2MoV的低温力学性能
Quenched and Tempered (Q+T) of 34CrNiMo6 Steel Heat 34CrNiMo6 round steel slowly to the temperature of 850°C; Soak at this hardening temperature quench in oil; Temper as soon as 34CrNiMo6 steels reach room temperature. Heat uniformly to the suitable temperature; Withdraw fro...
Quenched and Tempered (Q+T) of 34CrNiMo6 Steel Heat 34CrNiMo6 round steel slowly to the temperature of 850°C; Soak at this hardening temperature quench in oil; Temper as soon as 34CrNiMo6 steels reach room temperature. Heat uniformly to the suitable temperature; Withdraw from the...
Q: What is your terms of payment ? A: Payment<=1000USD, 100% in advance. Payment>=1000USD, 30% T/T in advance ,balance before shippment. If you have another question, pls feel free to contact us as below: Send your m...
34CrNiMo6钢调质(Q+T) 将34CrNiMo6圆钢缓慢加热至850℃; 在此硬化温度下浸泡在油中淬火; 34CrNiMo6 钢一达到室温就回火。 均匀加热至合适温度; 从炉中取出并在空气中冷却。 通常回火温度为600°C,具体视实际要求而定。 锻造DIN 34CrNiMo6 / 1.6582 钢
EN 34CrNiMo6 钢是一种重要的合金工程钢等级,符合 BS EN 10083-3:2006。通常我们以 Q+T 状态或热轧状态供应 34CrNiMo6 钢。 硬度:28-32HRC(Q+T状…
DIN 34CrNiMo6 (1.6582) 圆棒 EN 34CrNiMo6 钢是BS EN 10083-3:2006中重要的合金工程钢牌号。通常我们供应 Q+T 状态或热轧状态的 34CrNiMo6 钢。 硬度:28-32HRC(Q+T条件) 提供热轧/QT 条件。 Chemical Composition Relevant Specifications and Equivalents...