屈服强度(屈服极限)(Tensile Strength, Yield):240 MPa(34800 psi) 断裂延伸率(Elongation at Break):55% 弹性模量(Modulus of Elasticity):193 GPa(28000 ksi) 热性能(Thermal Properties) 热膨胀系数(CTE, linear): 16.0 μm/m-℃(@Temperature 0-100 ℃) 16.2 μm/m-℃(@Temperature 0-315 ℃) 17.5...
Physical Properties 316/316L/316H stainless steel in the Annealed Condition at -20°F to +100°F AlloyUNS DesignationSpec.Tensile Strength (psi)Tensile Strength (MPa)Tensile Strength (ksi)Yield Strength (psi)Yield Strength (MPa)Yield Strength (ksi)Elongation in 2 inches (min.) %Grain Size Re...
Stainless Steel Mechanical Properties Grade Tensile Strength Yide Strength Elogation Hardness Soluction Annealing kgf/mm²(N/mm²) kgf/mm²(N/mm²) % HRB(HV) ºC ASTM TP 304 ≥53 (515) ≥21 (205) ≥35 ≤90 (200) 1040ºC-1150ºC TP 304L ≥50 (485) ≥17 (170) Wat...
Mechanical Properties Tensile strength90,000 psi Yield strength45,000 psi Elongation in Two Inches35% Reduction in Area60% Modulus of Elasticity28,000,000 psi Density.290 lbs/cubic inch The information on this web site is intended for guidance only. Since we gathered technical data from various...
Stronger than 304 stainless steel View ProductsRequest a Quote Mechanical Properties (Typical Min.) 316316L Tensile Strength75,000 PSI70,000 PSI Yield Strength30,000 PSI25,000 PSI Elongation40%40% Chemical Composition Element316 Percentage (%)316L Percentage (%) ...
4: 316L steel mechanical properties The mechanical properties mainly include tensile strength, yield strength, elongation, area or reduction, hardness, impact value, non-metalic inclusion etc. Different heat treatment, the mechanical properties will be different, such as...
316S33 (1.4436) stainless steel is added with hydrogen on the basis of 316, but the carbon content is at its upper limit, which is mostly used for the requirements of thermal strength properties rather than molybdenum containing steel
Condition Yield Strength (ksi) min. Tensile Strength (ksi) min. Elongation % min. in 2 in. <0.015 in. ≥0.015 in. 1/4 Hard 75 125 10 10 1/2 Hard 110 150 6 7Physical Properties Physical properties for Type 316/316L stainless steel...
Mechanical PropertiesMetricEnglishComments Hardness, Brinell187187 Tensile Strength, Ultimate520MPa75400psi Tensile Strength, Yield205MPa29700psi Elongation at Break40 %40 % Rupture Strength21.0-22.0MPa @Temperature 750 °C, Time 3.60e+8 sec3050-3190psi ...
Condition Yield Strength (ksi) min. Tensile Strength (ksi) min. Elongation % min. in 2 in. <0.015 in. ≥0.015 in. 1/4 Hard 75 125 10 10 1/2 Hard 110 150 6 7Physical Properties Physical properties for Type 316 / 316L stainless steel Property 316/316L Data Density, lb/in3 0.290...