The temperature dependence of the heat capacity C p o = f ( T ) 2 of 2-ethylhexyl acrylate was studied in an adiabatic vacuum calorimeter over the temperature range 6–350 K. Measurement errors were mainly of 0.2%. Glass formation and vitreous state parameters were determined. An isothermic...
For this purpose emulsion, polymerization process was conducted for the preparation of an acrylic copolymer containing 2-ethylhexylacrylate, vinyl acetate, methacrylic acid (MAcid), and acrylonitrile using potassium persulfate as an initiator. The monomers were feeding different ratios with increasing 2% ...
As a higher alkyl acrylate comonomer, 2 Exylhexyl Acrylate uses a range of factors to impart a glass transition temperature that is well below room temperature (homopolymer Tg is – 65°C), flexibility, elasticity, and hydrophobic qualities. Unique features the compound contributes to copolymer ...
Poly(2-ethylhexyl acrylate)Block copolymersAtom transfer radical polymerizationThe controlled synthesis of low-Tg poly(2-ethylhexyl acrylate) (P2EHA) and derived random, block and blocky gradient copolymers via atom transfer radical polymerization (ATRP) is described. After optimizing the reaction ...
polyurethanePolydimethylsiloxane (PDMS) was grafted onto polyurethane (PU) to form a P series, and 2-ethylhexyl acrylate (EHA) was graft-polymerized onto PU to form an E series. The spectroscopic, thermal, tensile, shape memory, and low-temperature flexibility properties of the P and E ...
This investigation reports the atom transfer radical copolymerization (ATRcP) of glycidyl methacrylate (GMA) and 2-ethylhexyl acrylate (EHA). Poly(glycidyl methacrylate) (PGMA) has easily transformable pendant oxirane group and poly(2-ethylhexyl acrylate) (PEHA) has very low Tg. They are the ...
plasticized polyvinyl chloride comprising 25 to 40% by weight of a vinyl ester of a alkanoic acid; 10-30% by weight ethylene; 20 to 30% by weight of di-2-ethylhexyl maleate or fumarate; 20 to 30% by weight of 2-ethylhexyl acrylate; and 1 to 10% by weight of a monocarboxylic acid....
Characterization of swelling behavior and elastomer properties of acrylate polymers containing 2-ethylhexyl and isobornyl estersSwelling propertiesOrganogelsProperties and characterizationIn this work, a comparative study of the swelling behavior of poly((1,7,7-trimethyl-2-bicyclo[2.2.1]heptanyl) prop-2-...
interpolymere of ethylene - vinyl acetate dioctyl maleate and 2-ethylhexyl acrylateAdhesive compositions having a Tg of -45 to -25 DEG C suitable for application to plasticized polyvinyl chloride comprising 25 to 40% by weight of a vinyl ester of a alkanoic acid; 10-30% by weight ethylene; ...
Ethylene Vinyl Acetate-Dioctyl Maleate-2-Ethylhexyl Acrylate InterpolymersAdhesive compositions having a Tg of -45 to -25掳C suitable for application to plasticized polyvinyl chloride comprising 25 to 40% by weight of a vinyl ester of a alkanoic acid; 10-30% by weight ethylene; 20 to 30% by...