Ti3SiC2/SiC复相陶瓷 1. The high temperature oxidation behavior of theTi_3SiC_2/SiC multiphase ceramicsfabricated by in-situ synthesis under hot isostatic pressing were studied. 利用热等静压原位合成技术制备了Ti3SiC2/SiC复相陶瓷,对其高温氧化行为进行了研究。
2) Al2O3/SiC composite ceramics Al2O3/SiC复相陶瓷 1. By pressureless sintering,Al2O3/SiC composite ceramics used in solar thermal power were prepared by micrometric Al2O3 and SiC powers. 以微米级氧化铝和SiC为原料,通过无压烧结工艺,制备出用于太阳能热发电的Al2O3/SiC复相陶瓷。
This thesis mainly consists of three aspects: synthesis of BN ceramic fibers from precursor, preparation of BN powders and hot-pressed BN-AlN ceramic composites. 本文对BN的研究主要包括三个方面:BN粉末的合成;先驱体法合成BN纤维;热压制备BN-AlN复相陶瓷。2...
Ti3SiC2/SiC复相陶瓷 1. The high temperature oxidation behavior of theTi_3SiC_2/SiC multiphase ceramicsfabricated by in-situ synthesis under hot isostatic pressing were studied. 利用热等静压原位合成技术制备了Ti3SiC2/SiC复相陶瓷,对其高温氧化行为进行了研究。
的BSTN复相陶瓷为钙钛矿相和钨青铜相两相稳定共存的复合相;在该范围以外,则为单一相的钛酸锶钡与Nb或铌酸锶钡与Ti的固溶体.复相陶瓷的介电性能取决于钙钛矿相和钨青铜相的相对含量及其固溶度,当组成y约为0.7时,介电常数达到最大值;随测试频率的提高,介电常数和损耗降低.复相陶瓷中钨青铜相的铁电/顺电相转变...
多孔Si_3N_4_SiO_2复相陶瓷及其性能_英文_
背景:陶瓷本身质地较脆,抗弯强度较小,在一定程度上限制了其在口腔修复中的应用。氧化锆陶瓷通过其相变增韧,具有较高的抗弯强度和断裂韧性,这一特点可以弥补传统全瓷修复体所存在的脆性问题。目的:利用纳米氧化锆粉体和磷酸镧复合,初步探索制备新型可切削氧化锆陶瓷。探索牙科可切削氧化锆/磷酸镧复相陶瓷制备烧结特性...
首次系统的给出了三种不同相结构的PZT陶瓷铁电畴的PFM图像,发现 PZT陶瓷电畴结构依赖于其相结构,三方的电畴为条状,四方的电畴在两个方向上的尺寸相当,相界的电畴同时含有三方和四方的畴构型。在四方相PZT陶瓷上观察到了180°铁电畴构型,未能观察到90°铁电畴构型,在三方相PZT陶瓷同时观察到了180°,70.5°和109...
很多调查确认了那陶瓷增强的出席 ( 胡须,纤维,微粒 ) 相当地可以影响铝合金的时效硬化行为。主要结果 are(1-7)(1)GP 或 GPB 区域构成在合成物被抑制; (2) the precipitation of metastable phases such as,S,or is accelerated in the composites;以及 (3) 时间需要达到高峰老化在被与被不加强的基本合金比...