名称:G1-03 ASTM G1-03 腐蚀试样的制备、清洗和评定 1 范围 1.1 本标准规定了基体金属试样的制备、腐蚀试验完成后腐蚀产物的去除方法和对腐蚀程度进行评定。主要规定了通过质量损失和测量腐蚀坑的大小进行腐蚀评定的方法。(警告—在大多数情况下,活性金属钛以及锆钛合金的腐蚀产物是一种紧密结合的氧化物,无法通过...
Designation: G1 − 03 (Reapproved 2011)Standard Practice forPreparing, Cleaning, and Evaluating Corrosion TestSpecimens 1This standard is issued under the f i xed designation G1; the number immediately following the designation indicates the year of originaladoption or, in the case of revision, ...
ASTM G1-03(2017)e1 引用标准 ASTM A262ASTM D1193ASTM D1384ASTM D2776ASTM G15ASTM G16ASTM G31ASTM G33ASTM G46ASTM G50ASTM G78 购买 正式版 给出的程序旨在去除腐蚀产物,而不显着去除基体金属。这样可以准确确定金属或合金在暴露于腐蚀环境期间发生的质量损失。在某些情况下,这些程序可能适用于金属涂...
标准号 中文名称 英文 G1-03 腐蚀试样的制备,清洗和评定 Standard Practice for Preparing, Cleaning, and Evaluating Corrosion Test Specimens G2-88(2002) 在750°F蒸汽中或在680°F水中锆,铪及其合金产品腐蚀检验法 Standard Test Method for Corrosion Testing of Products of Zirconium, Hafnium, and Their ...
Designation: G1 − 03 (Reapproved 2011)Standard Practice forPreparing, Cleaning, and Evaluating Corrosion TestSpecimens 1This standard is issued under the fixed designation G1; the number immediately following the designation indicates the year of originaladoption or, in the case of revision, the ...
ASTM材料目录(G部分)标准号G1-03G2-88(2002)中文名称腐蚀试样的制备,清洗和评定在750°F蒸汽中或在680°F水中锆,铪及其合金产品腐蚀检验法在673°K蒸汽中或在633°K水中锆,铪及其合金产品腐蚀检验的方法(米制)腐蚀检验中用的电化测量的常规方法在工厂设备中进行腐蚀试验指南作静电位标记和动电位阳极极化测量的...
e1 Standard Practice for Preparing Cleaning and Evaluating Corrosion Test Specimens《腐蚀试验样本制备 清洗和评估的标准实施规程》.pdf》由会员分享,可在线阅读,更多相关《ASTM G1-2003(2017)e1 Standard Practice for Preparing Cleaning and Evaluating Corrosion Test Specimens《腐蚀试验样本制备 清洗和评估的标准...
标准号:ASTM G1-2003 中文标准名称:腐蚀试样的制备、清洁处理和评定用标准实施规范 英文标准名称:Standard Practice for Preparing, Cleaning, and Evaluating Corrosion Test Specimens 标准类型:H25 发布日期:1999/12/31 12:00:00 实施日期:1999/12/31 12:00:00 ...
ASTM标准目录_专业资料。ASTM标准目录 G1-03 Standard Practice for Preparing, Cleaning, and Evaluating Corrosion Test Specimens G2/G2M-06 Standard Test Method for Corrosion Testing of Products of Zirconium, Hafnium, an G3-89(2004) Standard Practice for Conventions Applicable to Electrochemical ...
8.25.1通量密度测量: 8.25.1.1 测试设备——直流场高斯计,分辨率为5高斯(g)和轴型探棒。 (1)活动区域直径为0.76±0.13 mm。 (2)活动区域与探棒端部距离为0.38±0.13 mm。 8.25.1.2 测试方法: (1)把探棒的端部贴着磁体的磁极面。对于磁性部件(无论磁体整个或部分嵌入玩具的部件中),把探棒的端部贴着部件...